Manufacturers (Origin): Shanghai Takahashi Grade: 8434 Processing Level: injection molding grade level characteristics: high flow, high gloss, high temperature resistant, anti-static products parameters: Performance Project test conditions [state] method of test data Data unit Basic properties Melting flow rate (230 ℃ / 3.8kg) 200 ℃, 3.8kg ASTM D-1238 3.9 g / 10min Mechanical properties Tensile yield strength 1/8 ", 5mm / min ASTM D-638 41 MPa tensile elongation at break 1 / 8 ", 5mm / min ASTM D-638 25% Tensile strength at break 1/8", 5mm / min ASTM D-638 32 MPa tensile yield elongation 1/8 ", 5mm / min ASTM D-638 2 % IZOD notched impact strength of 73 ° F (23 ℃) 1/8 ", 23 ℃ ASTM D-256 28 KJ / m2 thermal performance of Vicat softening point (120 ℃ / 10hr) 1/8", 50 ℃ / hr ASTM D -1525 106 ℃ Product Description: Note: High gloss high heat